Yixing Hengyuan Ceramic Technology Co., Ltd.
Bear a heavy burden and cover a long distance,persist with unremitting efforts.
Add to Cart
The manufacturing process of alumina ceramic tubes usually includes steps such as powder preparation, molding, sintering, and post-treatment. Firstly, high-purity and fine-grained alumina powder is obtained through powder preparation process. Then, the powder is prepared into tubular products with a certain shape and size using molding technology. Next, the formed aluminum oxide tube is subjected to high-temperature heat treatment through sintering process to promote particle bonding and form a dense ceramic material. Finally, post-processing techniques such as polishing and grinding are carried out to make the surface of the alumina ceramic tube smooth and even.
| Naterial | Unit | A95% Alumina Ceramics | A97% Alumina Ceramics | A99% Alumina Ceramics | A99.7% Alumina Ceramics |
| Density | g/cm³ | 3.6 | 3.72 | 3.85 | 3.85 |
| Flexural Strength | Mpa | 290 | 300 | 350 | 350 |
| Compressive Strength | Mpa | 3300 | 3400 | 3600 | 3600 |
| Modulus of Elasticity | Gpa | 340 | 350 | 380 | 380 |
| Impact Resistance | MPam1/2 | 3.9 | 4 | 5 | 5 |
| Weibull Modulus | M | 10 | 10 | 11 | 11 |
| Vickers Hardulus | HV0.5 | 1800 | 1850 | 1900 | 1900 |
| Thermal Expansion Coefficient | 10-6K-1 | 5.0-8.3 | 5.0-8.3 | 5.4-8.3 | 5.4-8.3 |
| Thermal Conductivity | W/Mk | 23 | 24 | 27 | 27 |
| Thermal Shock Resistance | △T℃ | 250 | 250 | 270 | 270 |
| *Maximum Use Temperature | ℃ | 1600 | 1600 | 1650 | 1650 |
| Volume Resistivity at 20℃ | Ω | ≥1014 | ≥1014 | ≥1014 | ≥1014 |
| Dielectric Strength | KV/mm | 20 | 20 | 25 | 25 |
| Dielectric constant | εr | 10 | 10 | 10 | 10 |