Under the general condition, the analyzed and fired substance is put into the alumina crucible or a bowl and then put into analyzing or firing equipment to be heated. Heating and cooling speed is different according to the characteristics of the equipment and products. A raw material for manufacturing the alumina crucible and the bowl is subjected to thermal expansion, and the alumina crucible and the sagger are easily cracked if the heating or cooling speed is overhigh, so that the speed had better be low to prolong the service life of the crucible and the bowl.
Features:
| Naterial | Unit | A95% Alumina Ceramics | A97% Alumina Ceramics | A99% Alumina Ceramics | A99.7% Alumina Ceramics |
| Density | g/cm³ | 3.6 | 3.72 | 3.85 | 3.85 |
| Flexural Strength | Mpa | 290 | 300 | 350 | 350 |
| Compressive Strength | Mpa | 3300 | 3400 | 3600 | 3600 |
| Modulus of Elasticity | Gpa | 340 | 350 | 380 | 380 |
| Impact Resistance | MPam1/2 | 3.9 | 4 | 5 | 5 |
| Weibull Modulus | M | 10 | 10 | 11 | 11 |
| Vickers Hardulus | HV0.5 | 1800 | 1850 | 1900 | 1900 |
| Thermal Expansion Coefficient | 10-6K-1 | 5.0-8.3 | 5.0-8.3 | 5.4-8.3 | 5.4-8.3 |
| Thermal Conductivity | W/Mk | 23 | 24 | 27 | 27 |
| Thermal Shock Resistance | △T℃ | 250 | 250 | 270 | 270 |
| *Maximum Use Temperature | ℃ | 1600 | 1600 | 1650 | 1650 |
| Volume Resistivity at 20℃ | Ω | ≥1014 | ≥1014 | ≥1014 | ≥1014 |
| Dielectric Strength | KV/mm | 20 | 20 | 25 | 25 |
| Dielectric constant | εr | 10 | 10 | 10 | 10 |